- Study on Lapping of Diamond Tool (3rd Report)
- ダイヤモンド工具の研磨に関する研究-3-単結晶ダイヤモンドの被研磨特性
- ダイヤモンド コウグ ノ ケンマ ニ カンスル ケンキュウ 3 タンケッショウ
- Anisotropy in Stock Removal of Single Crystal
- 単結晶ダイヤモンドの被研磨特性
この論文をさがす
抄録
This paper deals with the lapping characteristics for crystallographic orientation of single crystal diamond. The rough diamonds were lapped by cast iron lap as well as steel lap and diamond wheels. The lapping removal depth, lapping force ratio (tangential force / normal force) and lapping temperature for lapping direction on the typical three planes were measured. Experimental results are as follows : the relationship between lapping removal depth and lapping force ratio was devided into the following two trend. In the lapping by cast iron lap and steel lap, at the easy lapping direction (i.e. {110}, <100>) lapping force ratio was small and lapping temperature was low, at the hard lapping direction ({110}, <110>) the former value was large and the latter was high respectively. On the other hand, in the lapping by diamond wheel, at the easy and hard lapping direction these two values changed conversely in the tendency of the cases by cast iron and steel lap.
収録刊行物
-
- 精密工学会誌
-
精密工学会誌 59 (2), 281-286, 1993
公益社団法人 精密工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204765827072
-
- NII論文ID
- 110001371292
-
- NII書誌ID
- AN1003250X
-
- ISSN
- 1882675X
- 09120289
-
- NDL書誌ID
- 3807703
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可