下部ベイナイト域で引抜き・等温保持したばね線の機械的性質

DOI Web Site Web Site 被引用文献3件 参考文献37件

書誌事項

タイトル別名
  • Mechanical Properties of Spring Wire Drawn and Tempered at Lower Bainite Region
  • カブ ベイナイトイキ デ ヒキヌキ トウオン ホジ シタ バネセン ノ キカイテキ セイシツ

この論文をさがす

抄録

Medium carbon spring steel containing Si (SWOSC-V) was aus-drawn and temperd at 543573K (lower bainite region) to obtain the wire with ausformed bainite structure. Aus-forming refined bainitic ferrite. Especially near surface, bainitic ferrite tended to align in one direction because of a large amount of redundant shear strain in drawing. The redundant shear strain also resulted in larger hardness near the surface especially in the cases of low drawing velocities and large die-cone angles. At center regions, the aus-formed bainite wires showed smaller hardness than that of a conventional oil quenched and tempered wire with tempered martensite structure possibly due to higher transformation temperature by heat generation during drawing. The aus-formed bainite wires had large amount of retained austenite up to 25%. The retained austenite transformed to martensite during shot-peening or fatigue testing, so that the aus-formed bainite wires showed good mechanical properties and fatigue strength comparable to those of the conventional wires. These results indicate that the present new and simple process (aus-drawing+tempering) could be applicable to practical use for spring wire production.

収録刊行物

  • 鉄と鋼

    鉄と鋼 85 (8), 605-612, 1999

    一般社団法人 日本鉄鋼協会

被引用文献 (3)*注記

もっと見る

参考文献 (37)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ