733~818Kにおける鉄と鉛-亜鉛融液との反応拡散

• 若松 良徳

  九州工業大学工学部

• 桝本 弘人

  九州工業大学大学院生(現:住友金属工業(株))

• 山根 政博

  九州工業大学工学部

• 大西 正已

  九州工業大学工学部

• 下崎 敏唯

  九州工業大学機器分析センター

書誌事項

タイトル別名

• Reaction Diffusion between Iron and Pb-Zn Melt at 733 to 818K
• 733 818K ニ オケル テツ ト ナマリ アエン ユウエキ ト ノ ハン

抄録

Pure Fe specimens were annealed in pure Zn and binary Pb-Zn melts at temperatures between 733 and 818K for various times. The kinetics of the reaction diffusion between the specimen and the melt was examined. In the case of the pure Zn melt, the Γ, Γ₁, compact δ₁ and palisade δ₁ phases were formed between the Fe specimen and the melt at temperatures higher than 778K, and the ζ phase as well as these four intermetallic phases was observed at temperatures lower than 768K. In the case of the binary Pb-Zn melt, however, the formation of the intermetallic phases with high zinc concentrations was inhibited with decreasing zinc content of the melt. At temperatures between 778 and 808K, fragmentation of the palisade δ₁ phase occurred during the annealing in the Pb-Zn melt with zinc content higher than 40 mass%.

収録刊行物

• 鉄と鋼

  鉄と鋼 82 (1), 75-80, 1996

  一般社団法人 日本鉄鋼協会

キーワード

• Iron
• lead zinc melt
• reaction diffusion
• fragmentary δ<SUB>1</SUB>
• Kirkendall effect

詳細情報

• CRID: 1390001205151331328
• NII論文ID: 110001481416
• NII論文ID: 10003280952
• NII書誌ID: AN00151251
• DOI: 10.2355/tetsutohagane1955.82.1_75
• ISSN: 18832954
• ISSN: 00211575
• NDL書誌ID: 3936815
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3936815
• Web Site: https://www.jstage.jst.go.jp/article/tetsutohagane1955/82/1/82_1_75/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可