- Siliconizing of Iron and Steel by Molten Magnesium Bath with Silicon Carbide Powder
- ヨウユウ マグネシウムヨク ト タンカ ケイソ フンマツ オ モチイタ テッコ
この論文をさがす
抄録
A molten magnesium bath was used to siliconize iron and steel specimens embedded in SiC powder for various periods at 973-1123K. The siliconized layer obtained was composed of Fe3Si phase as the matrix and SiC phase as dispersed particles.<BR>Therefore, a hard composite layer, as high as 820 of Vickers hardness number, could be obtained.<BR>The thickness of the layer varied depending on the siliconizing temperature and time. Then the thickness was measured as to iron specimens siliconized with 5μm-SiC powder and then the diffusion coefficient was calculated as, <BR>D=34.22×10-4exp[-186.30(kJ/mol)/RT] (m2/s). The thickness of the layer could also vary with SiC powder size of 2 to 40μm, the smaller in the size, the thicker in the layer. However, SiC powder of 5μm was thought to be suitable practically.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 83 (7), 442-447, 1997
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680161029376
-
- NII論文ID
- 110001481698
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 4249022
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可