- Microstructural Change during Isothermal Aging in High Manganese Austenitic Steels
- コウ Mn オーステナイト コウ ノ コウオン ヘンタイ ニ トモナウ ソシキ
この論文をさがす
抄録
Microstructural change during isothermal aging has been investigated in 13%Mn-0.9%C and 22%Mn-0:6%C steels by means of optical and electron microscopy and X-ray diffractometry.<BR>High manganese austenitic steels undergo three kinds of reactions during isothermal aging ;(1) grain boundary precipitation of carbide, (2)precipitation of platelet carbide within austenite(γ) grains and (3)formation of lamellar structure through eutectoid transformation (γ→ferrite(α)+carbide).In 13%Mn-0.9%C steel, all of the reactions occur and the carbide concerning the reactions is M3C in any case. On the other hand, in 22%Mn-0.6%C steel, only two of them occur ; grain boundary precipitation of M23C6 carbide (not M3C) and the eutectoid transformation (γ→α+M3C). Besides, both of the two reactions in 22%Mn-0.6%C steel were effectively suppressed due to the chemical composition ; high Mn and low C content.<BR>Eutectoid transformation proceeds by being supplied carbon from untransformedγ, so that this results in the shortage of carbon in untransformedγduring isothermal aging and theγphase undergoesγ→ε(hcp) martensitic transformation on the following cooling.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 84 (4), 309-314, 1998
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680161415808
-
- NII論文ID
- 110001481811
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 4437267
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可