- Disbonding of Overlay Weldment in V-modified 21/4Cr-1Mo Steels
- V テンカ 21 4Cr 1Mo コウ ノ ニクモリ ヨウセツブ ノ ハクリ
この論文をさがす
抄録
The effect of V on the disbonding between 2 1/4Cr-1Mo steels and austenitic stainless steel overlay was studied metallurgically. The addition of V into the base metal increases resistance to disbonding significantly. STEM and EDX observation showed that the fine precipitates are different in morphology, distribution and composition between V-modified and ordinary steels. The analyses of hydrogen diffusion and hydrogen evolution indicated that the fine precipiates in V-modified steel trap hydrogen and as a result increase the solubility of hydrogen and decrease the diffusion of hydrogen. Theoretical calculation of hydrogen distribution during cooling from high temperature and high pressure conditions showed that both diffusion and solubility of hydrogen in the base metal affects the concentration of hydrogen at the interface between base metal and stainless steel overlay. It is concluded that the fine precipitates in V-modified steel increase resistance to disbonding by reducing the concentration of hydrogen at the interface during cooling.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 75 (5), 798-805, 1989
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205184198144
-
- NII論文ID
- 110001492383
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 3235934
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可