抄録
The purpose of this paper is to understand controlling factors of separations parallel to the rolling plane developed in charpy specimens when rolling is extended in α+γ two phase regions.<BR>Main results are as follows:<BR>1) Separation were found to be enhanced by the development of {100} and {111} textures, the formation of large texture bandings consisted of a group of ferrite grains having a common crystallographic orientation, and the presence of the local plastic flow at the notch root preceding complete fracture.<BR>2) Separations were found to increase the area of intergranullar fracture as the texture developes.<BR>On the basis of these results it is suggested that separations may be formed by the initiation of the crack along the interface between {100} bandings and {111} bandings resulting from the anisotropic plastic flow of these bandings.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 68 (3), 435-443, 1982
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205181977216
-
- NII論文ID
- 110001870490
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 2443813
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可