NMR and Magnetic Studies of Mechanically Alloyed Co<sub>30</sub>M<sub>70</sub>(M=Cu, Ag, Au)
-
- Hiraoka Koichi
- Faculty of Engineering, Ehime University
-
- Sasaki Yasuhiro
- Faculty of Engineering, Ehime University
-
- Tomiyoshi Shoichi
- Faculty of Engineering, Ehime University
書誌事項
- タイトル別名
-
- NMR and Magnetic Studies of Mechanically Alloyed Co30M70 (M=Cu, Ag, Au)
この論文をさがす
抄録
Zero-field 59Co NMR, X-ray diffraction (XRD) and magnetization measurements have been made to investigate the mechanical alloying (MA) of ferromagnetic Co30M70 (M=Cu, Ag and Au) powder as a function of milling time (MT). The MA in Co30Cu70 proceeds rapidly with increasing MT by both the processes of dissolving Cu in the Co matrix and Co in the Cu matrix and is nearly completed for MT=100 h. In Co30Ag70 the MA hardly proceeds even for MT=300 h or more. The MA in Co30Au70 proceeds much more slowly than that in Co30Cu70 with increasing MT up to 150 h and takes place rapidly for MT≈200 h. The magnetizations and NMR spectra of the Co30Cu70 and Co30Au70 samples for MT=200 h are similar to each other, indicating that both the samples form similar supersaturated alloys. NMR results of the Co30M70 samples milled for MT=200 h show large spin fluctuations of Co atoms, which are due to fine sizes of clusters, suggesting that the samples milled for long times consist of nanometer-size clusters.
収録刊行物
-
- Journal of the Physical Society of Japan
-
Journal of the Physical Society of Japan 74 (9), 2598-2603, 2005
一般社団法人 日本物理学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679164889344
-
- NII論文ID
- 210000105654
- 110002245749
- 130004539417
-
- NII書誌ID
- AA00704814
-
- BIBCODE
- 2005JPSJ...74.2598H
-
- ISSN
- 13474073
- 00319015
-
- NDL書誌ID
- 7439643
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可