BIOMIMETIC COATING OF BONE-LIKE APATITE ON GLASS BEADS
-
- OSAKA Akiyoshi
- Biomaterials Lab, Faculty of Engineering, Okayama University
-
- TAKEMOTO Shinji
- Biomaterials Lab, Faculty of Engineering, Okayama University
-
- HAYAKAWA Satoshi
- Biomaterials Lab, Faculty of Engineering, Okayama University
-
- OHTSUKI Chikara
- Biomaterials Lab, Faculty of Engineering, Okayama University
この論文をさがす
抄録
Soda lime glass beads were chemically treated by either an aqueous solution of NaOH (3mol/l) or a hydrogen peroxide solution (30vol%) containing TaCl5 in 5×10-3mol/l or by both of them. The treated samples were soaked up to 14 days in a simulated body fluid (SBF): Na+ 142.0, K+ 5.0, Ca2+ 2.5, Mg2+ 1.5, Cl- 147.8, HCO3- 4.2, HPO42- 1.0, SO42- 0.5 (in 10-3mol/l), or in another solution 1.5 times as concentrated as SBF (1.5SBF). The SBFs were kept at 36.5°C and at 7.25 in pH. Apatite was deposited on the samples treated with the NaOH solution, the H2O2/Ta solution, and both of them before soaking in 1.5SBF. Ta(V) ions were present on not only the samples treated with the H2O2/Ta solution but those treated with both NaOH and the H2O2/Ta solutions. It was concluded that Ta(V) ions on the surface layer had ability of inducing apatite deposition, and the ability was enhanced by the coexistence with silanol groups.
収録刊行物
-
- 材料
-
材料 47 (3Appendix), 60-63, 1998
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680420182656
-
- NII論文ID
- 110002283945
-
- NII書誌ID
- AA11046472
-
- ISSN
- 18807488
- 05145163
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可