BaLaInMO<sub>5.5</sub>(M=Sc, GaとIn) とBaLaIn<sub>2-x</sub>Sc<sub>x</sub>O<sub>5.5</sub>(x=0.1, 0.2と0.3) の酸化物イオン導電性について
書誌事項
- タイトル別名
-
- Oxide-Ion Conductivity of BaLaInMO5.5 (M=Sc, Ga and In) and BaLaIn2-xScxO5.5 (x=0.1, 0.2 and 0.3)
この論文をさがす
抄録
Solid solutions of BaLaIn2O5.5 and BaLaInMO5.5 that formed by partial replacement of In by Sc and Ga have a cubic perovskite structure. The Sc3+- and Ga3+-doped compounds, which had almost the same electrical conductivities, exhibited lower conductivities than the parent compound BaLaIn2O5.5 in the temperature range from 573 to 1273K. The Ga compound showed a transference number, ti, of unity at both high and low oxygen partial pressures in the temperature range from 973 to 1273K. As for the Sc compound kept at 973-1273K, a ti of nearly unity was observed at low oxygen partial pressure, while the ti was slightly lower than unity at high oxygen partial pressures at higher temperatures. The In compound had a ti of almost unity at high oxygen partial pressure, whereas the number decreased to a value less than 0.9 at low partial pressures of oxygen. The stepwise increase in the Sc content from 0.1 to 1.0 in BaLaIn2-xScxO5.5 caused a monotonic decrease in conductivity. The decrease in conductivity and the increase in activation energy caused by Sc3+ and Ga3+ doping were ascribed to the partial ordering of originally disordered oxygen vacancies and a decrease in the size of the triangle formed by two A-site cations and one B-site cation, through which the oxide ion proceeds, respectively.<br>
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 111 (1298), 729-732, 2003
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205249731328
-
- NII論文ID
- 110002288112
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 6725088
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可