CeO<sub>2</sub> 微粒子の緻密化における焼結曲線の屈曲

DOI 機関リポジトリ Web Site Web Site 被引用文献2件 参考文献30件
  • 小澤 正邦
    名古屋工業大学セラミックス基盤工学研究センター

書誌事項

タイトル別名
  • Sintering Curve Inflection in Densification of Fine CeO2 Powders at High Temperature

この論文をさがす

抄録

The sintering behavior of fine cerium dioxide (CeO2) powders from direct homogeneous precipitation using hexamethylenetetramine was examined by monitoring the continuous shrinkage of powder compacts during heating from 30 to 1700°C. Depending on the pre-heat-treatment condition of powders, the sintering curves of two starting powder compacts showed different shrinkage behavior. A powder heated at 650°C showed a normal sintering curve (S-type) with the highest shrinkage rate at around 1000°C. However, a powder heated at 350°C showed an extremely high shrinkage rate with inflection points in the sintering curve at 1300-1500°C. We analyzed the microstructure, pore structure and the secondary particle size of sintered bodies after sintering curve inflection. Grains 0.08 μm in size were roughly packed one another in the microstructure at 900°C after local sintering in the interior part of aggregated particles. The rapid shrinkage after rearrangement started at higher temperatures of 1300-1500°C, inducing large grain growth. The combination of rapid rearrangement and grain growth, which resulted in a sintering curve inflection, was assumed at temperatures as high as 900-1500°C.<br>

収録刊行物

被引用文献 (2)*注記

もっと見る

参考文献 (30)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ