- Quantitative Evaluation of Stress-Enhanced Corrosion on Glass Surface Using Vickers Indentation Method (Part 1) - Application to Some Glasses and Aqueous Solutions.
- ガラス ヒョウメン ニ タイスル オウリョク フショク サヨウ ノ ビッカースアッシ オシコミ ホウ ニ ヨル
- Application to Some Glasses and Aqueous Solutions
- 種々のガラス及び水溶液への適用
この論文をさがす
抄録
In order to make a quantitative evaluation of stress-enhanced corrosion on glass surface in aqueous solutions, an indentation method was adopted. Using this technique, the stress corrosion limit, KSCC, was measured in three different glasses, a soda-lime silicate glass and two kinds of alumino-silicate glasses. Influence of a surface active agent on the stress corrosion limit of soda-lime silicate glass was also estimated using soda kaplinate acid solution. The present results can be summarized as follows: (1) The indentation method can be generally used provided that a median/radial crack can be introduced on the glass surface, and it enables to distinguish subtle differences in the extent of the corrosion process. (2) Accurate KSCC data can be obtained within a 3% standard deviation. (3) By the indentation method the KSCC can be estimated in small specimens or at localized parts.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 107 (1241), 31-35, 1999
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205248024704
-
- NII論文ID
- 110002289611
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 106791
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可