- Temperature Dependence of Vickers Hardness for TeO2-Based and Soda-Lime Silicate Glasses.
この論文をさがす
抄録
The temperature dependence of Vickers hardness (H) of TeO2-Based glasses such as 15Na2O⋅15ZnO⋅70TeO2 as host glasses for rare-earth doped optical amplifier was measured from room temperature to the glass transition region. The following features were found; (1) crack formation under the indenter easily occurs, the Vickers hardness at room temperature being around 3GPa; (2) the temperature coefficient of the hardness, dH/dT, is around -4.5×10-3GPa·K-1; (3) the relative change of hardness with temperature is closely related to thermal expansion coefficient, and hardness sharply decreases in the glass transition region. It was demonstrated that TeO2-Based glasses are fragile even from the point of view of mechanical properties. The reason for poor mechanical performance in TeO2-Based glasses is their weak bond strength and open atomic packing structures. The hardness (H=4.8GPa) of a transparent glass-ceramic (with nanocrystalline particles) of 15K2O⋅15Nb2O5⋅70TeO2 showing second harmonic generation is much larger than that of the precursor glass (H=3.3GPa), meaning that the improvement in the fragile character of TeO2-Based glasses is due to crystallization. A soda-lime silicate glass of 14Na2O⋅13CaO⋅73SiO2 has a value dH/dT=-6.5×10-3GPa·K-1, and in contrast to TeO2-Based glasses, its hardness decrease in the glass transition region is gradual, and a value H≈2GPa is obtained even at the glass transition temperature.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 107 (1252), 1140-1145, 1999
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205249572608
-
- NII論文ID
- 110002289707
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 4929624
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可