- Interaction of Si<sub>3</sub>N<sub>4</sub> with Mn under Ar or N<sub>2</sub> Atmosphere
- Ar オヨビ N2 フンイキカ デ ノ Si3N4 ト Mn ト ノ ハンノウ
この論文をさがす
抄録
In relation to the joining of silicon nitride ceramics to metal, the reaction products and reaction mechanism between Si3N4 and Mn have been investigated in Ar or N2 at temperatures from 1073 to 1573K. Using an Si3N4-Mn powder mixture, the reaction rate was determined thermogravimetrically, and the reaction products were examined by X-ray diffraction. Under an Ar atmosphere, from 1223 to 1423K, MnSiN2, Mn0.815Si0.815 and Mn3Si were produced, and above 1423K, MnSiN2 disappeared. At higher temperatures and on prolonged heating, the suicide composition changed in the following order: Mn0.815Si0.185, Mn3Si, Mn5Si3, and MnSi. Under an N2 atmosphere, the reaction between Mn, Si3N4 and N2 produced Mn nitrides and MnSiN2. Below 1223K, the reaction products were Mn6N2.58 and Mn4N. At higher temperatures, MnSiN2 appeared, while Mn nitrides disappeared. Above 1423K, only MnSiN2 was produced. By relating these results to TG measurements, a full understanding of the reaction mechanism between Si3N4 and Mn was acquired.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 103 (1202), 1027-1032, 1995
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205277157632
-
- NII論文ID
- 110002291804
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 3640452
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可