- Sinterability and Mechanical Properties of TiB<sub>2</sub> without Additives
- ジョザイ ムテンカ TiB2 ノ ショウケツセイ ト リキガクテキ セイシツ
この論文をさがす
抄録
A commercial TiB2 powder with the grain size of 2μm was milled by an attriter and the powder having the average grain size of 0.9μm and the oxygen content of 3.4 mass% was obtained. Sinterability of the powder without additives and mechanical properties of hotisostatically pressed compacts were investigated. The density of fired compacts improved with rising firing temperature. However, compacts with densities approaching 100% were difficult to obtain by pressureless firing. Abnormal grain growth with cracks and residual pores occurred in the compact fired at 2000°C and its density was 92%. A compact having 99.5% density could be obtained by firing at 1800°C and sequential hot isostatic pressing with encapsulation at 1700°C. Fracture toughness, 3-point bending strength and Vickers hardness of the hot-isostatically pressed compact were 3.3 MPa·m1/2, 420MPa and 2500, respectively.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 103 (1202), 1077-1081, 1995
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680253884288
-
- NII論文ID
- 110002291814
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 3640502
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可