- A remaining life prediction method on the basis of micro-crack initiation and growth behavior under creep-fatigue in plain specimen of 316 stainless steel.
- SUS316 コウ ヘイカツザイ ノ クリープ ヒロウカ ニ オケル ビシ
この論文をさがす
抄録
To assure high-temperature component safety and reliability, a life prediction method has been developed. The method is based on the micro-crack growth rate and the microcrack distribution.<br>Strain controlled low-cycle fatigue tests were carried out on the plain specimens of SUS 316 at 923K in air and the initiation and growth behavior of surface micro-cracks were observed.<br>The results obtained are summarized below.<br>(1) The creep-fatigue life is governed by micro-crack growth.<br>(2) A linear relationship is observed between the logarithms of main surface crack length and the life ratio, N/Nf, for various strain loading conditions.<br>(3) The distribution of micro-crack length obeys the Weibull distribution.<br>Moreover, the maximum crack length in an area larger than the sample area can be estimated with a help of the statistics of extremes. Therefore, the remaining life of high-temperature components may be accurately predicted by measuring the distribution of surface micro-crack length in critical parts.
収録刊行物
-
- 材料
-
材料 35 (389), 170-175, 1986
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680369883904
-
- NII論文ID
- 110002296740
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DyaL28XhvFSlu7w%3D
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 3070531
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可