• Quantitative Evaluation of Applied Stress by Surface Roughness for Fatigue Fracture.
• ヒロウ ハメン アラサ ニ モトズク サヨウ オウリョク スイテイ

抄録

Quantitative evaluation of applied stress by fractography is not always easy if fatigue striations are not seen on the fatigue fracture surface. The authors have often experienced such a problem in case of industrial machines which failed under low vibrational stress. In this report, the quantitative characterization of the fatigue crack surface created by low stress amplitude is attempted. A good correlation between the proposed surcace roughness parameter (S₁) and the stress intensity factor range (ΔK) was obtained for low ΔK level. This technique is expected to be a supplemental method of quantitative stress evaluation of fractured component.

収録刊行物

• 材料

  材料 40 (453), 712-717, 1991

  公益社団法人 日本材料学会

キーワード

• Fatigue fracture surface
• Surface roughness
• Roughness parameter
• Applied stress
• Fractography

詳細情報

• CRID: 1390001205393547008
• NII論文ID: 110002298473
• NII書誌ID: AN00096175
• DOI: 10.2472/jsms.40.712
• ISSN: 18807488
• ISSN: 05145163
• NDL書誌ID: 3713002
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3713002
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可