フェライト・パーライト鋼の硫化水素割れ破面について

DOI Web Site

書誌事項

タイトル別名
  • On the Fracture Surface of Hydrogen Sulfide Cracking
  • フェライト パーライト コウ ノ リュウカ スイソ ワレ ハメン ニ ツイテ

この論文をさがす

抄録

The fracture surfaces of ferritic-perlitic steel caused by hydrogen induced cracking (HIC) and sulfide stress cracking (SSC) under the wet H2S environment were investigated by a scanning electron microscope. It was clarified that HIC and SSC were caused by hydrogen embrittlement. The cracks of HIC initiated around the nonmetallic inclusions (MnS) and they grew in a step-wise manner by connecting each other. On the other hand, the process of SSC took place as follows; the separated small cracks of HIC were connected by the cracks perpendicular to the stress axis. The fracture due to hydrogen embrittlement exhibited some characteristic fracture patterns, such as a river like pattern, flat pattern and so on. It was supposed that these fracture patterns were formed depending on the crystallographic orientation of grains. The striation type pattern was observed on the river like pattern as well as on the flat pattern. This striation type pattern seemed to correspond to the discontinuous propagation of hydrogen embrittlement cracking. In order to determine the sharp of the river like pattern, the stereo-matching technique was applied and it was found that this pattern could be classified into three types.

収録刊行物

  • 材料

    材料 27 (292), 81-86, 1978

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ