ＡＥ法による短繊維強化ＡＢＳ複合材料の破壊機構の解明に関する研究　繊維含有率の影響

• 鈴木 惠

• 木田 外明

• 宮下 寿徳

• 籠谷 陽介

• 菱川 英海

• 中西 博

書誌事項

タイトル別名

• Fracture Mechanisms of Short-Fiber-Reinforced ABS Composites by AE Technique. Effect of Fiber Content.
• AEホウ ニ ヨル タンセンイ キョウカ ABS フクゴウ ザイリョウ ノ ハ

抄録

Two specified loads, P_b and P_c, of short-fiber-reinforced ABS composites with various fiber contents are determined by the stress intensity factor method. The loads of P_b and P_C determined by this method are in good agreement with loads determined by the AE energy gradient method. The damage at the notch tip is observed through a monitor microscope at or near the loads of P_b and P_C. The fiber breakage estimated from AE frequency analysis at the loads is considered to be the dominant factor of the damage mode. It was found that the loads of P_b and P_c are important parameters to clarify the fracture mechanisms of the composites.

収録刊行物

• 日本機械学会論文集Ａ編

  日本機械学会論文集Ａ編 60 (576), 1779-1785, 1994

  一般社団法人 日本機械学会

キーワード

• Short-Fiber-Reinforced ABS Composites
• Fracture Mechanisms
• AE Technique
• Monitor Microscope
• Frequency Analysis
• Damage

詳細情報

• CRID: 1390282679424186752
• NII論文ID: 110002371948
• NII論文ID: 20000184025
• NII書誌ID: AN0018742X
• DOI: 10.1299/kikaia.60.1779
• ISSN: 18848338
• ISSN: 03875008
• NDL書誌ID: 3887416
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3887416
• Web Site: http://www.jstage.jst.go.jp/article/kikaia1979/60/576/60_576_1779/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可