粒界破壊抵抗分布モデルによるクリープ疲労微小き裂の発生と初期伝ぱのシミュレーション

DOI Web Site Web Site 被引用文献2件

書誌事項

タイトル別名
  • Simulation of initiation and early propagation of creep-fatigue small cracks based on the model of random fracture resistance of grain boundaries.
  • リュウカイ ハカイ テイコウ ブンプ モデル ニ ヨル クリープ ヒロウ ビシ

この論文をさがす

抄録

A stochastic model and a method of simulation of the initiation and the early propagation of creep-fatigue small cracks along grain boundaries were proposed. In the model, grain boundaries between two adjacent triple points were projected and linked on a straight line perpendicular to the applied stress axis, and their length was given as random variables of a normal distribution. The grain boundaries had their own fracture resistances, the magnitudes of which were given as uniform random numbers. The fracture resistance of each grain boundary decreased by a constant magnitude corresponding to the driving force of one fatigue cycle. When the resistance become zero or a negative value, the grain boundary was assumed to fracture and to yield an intergranular facet of small crack. Based on this model, a numerical calculation was done for a smooth specimen of 304 stainless steel subjected to the slow-fast strain cycle of 1%-total strain range at 923K in a vacuum. The result of simulation on crack density, cumulative probability of crack length, and crack propagation rates coincided with the experimental results.

収録刊行物

被引用文献 (2)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ