- Changes in Electrochemical Properties of Directionally Solidified Ni-base Superalloy Due to Creep and Damage Evaluation.
- 1ホウコウ ギョウコ Niキ チョウゴウキン ノ クリープ ニ トモナウ デン
この論文をさがす
抄録
Changes in electrochemical properties of directionally solidified Ni-base superalloy CM 247 LC due to creep have been investigated. The electrochemical polarization technique has been applied to creep-ruptured and creep-interrupted specimens under various creep condition in order to examine a detectability of creep damage. Experimental results on electrochemical polarization measurements revealed that the peak current density "Ip" and "Ipr" which appeared at a specific potential during potentiodynamic polarization reactivation measurements in dilute glyceregia solution increased with increased thermal history and showed a good correlation with Larson-Miller Parameter value. Ip and Ipr value reflected both a thermal aging effect and a stress effect, and increased with a creep life fraction. The increases in Ip and Ipr were mainly corresponded to increases in preferential dissolution rate of γ' phase at γ/γ' interface. This preferential dissolution was considered as a result from degradation of corrosion resistance of γ'phase at γ/γ'interface which may be attributable to creep damage accumulation. As a consequence, the creep damage in CM 247 LC can be quantitatively evaluated by the electrochemical technique.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 64 (623), 1997-2004, 1998
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679424799232
-
- NII論文ID
- 110002374674
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 4527028
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可