- Evaluation of the Fiber/Matrix Interfacial Properties under Static and Fatigue Loading using Model Composites
抄録
Single fiber pull-out tests under static and fatigue loading were carried out to investigate the influence of wet environment on the interfacial strength and on the propagation properties of interfacial debonding of an aramid/epoxy system using the specially designed model composites. The fiber/matrix interfacial strength was decreased by 26% after 7 week immersion in deionized water at 80℃. In dry air, interfacial debonding under fatigue loading propagated faster than in laboratory air, whereas it hardly propagated in wet air. When the length of interfacial debonding became longer, the fatigue propagation rate of interfacial debonding slowed down and retarded irrespective of the environment although a constant fatigue load was applied to the sample. This behavior was considered to be owing to the friction stress on the debonded wakes.
収録刊行物
-
- 材料力学部門講演会講演論文集
-
材料力学部門講演会講演論文集 2003 (0), 189-190, 2003
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206066096512
-
- NII論文ID
- 110002489026
-
- ISSN
- 24331287
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可