Mechanical Behavior of Ti-48Al-2Mn-2Nb Alloy Produced by Centrifugal Spray Deposition(Mechanical Behavior of Materials 2)
-
- Chen Wenzhe
- College of Materials Science &Engineering, Fuzhou University
-
- Peng Kaiping
- College of Materials Science &Engineering, Fuzhou University
-
- Chen Xingpin
- College of Materials Science &Engineering, Fuzhou University
-
- Qian Kuang-Wu
- College of Materials Science &Engineering, Fuzhou University
抄録
The mechanical behavior of Ti-48Al-2Mn-2Nb alloy produced by centrifugal spray deposition (CSD) was investigated. Tensile, compression and fracture toughness tests of CSD Ti-48Al-2Mn-2Nb alloy were carried out at room temperature (RT), and the comparison was made with the ingot metallurgy (IM) Ti-48Al-2Mn alloy at RT, as well as at 600 and 800℃. The results show that CSD Ti-48Al-2Mn-2Nb alloy exhibits a better elongation of 2.8%, and excellent compression properties with compressive strength of 2210MPa and compressive ratio of 33.9% at room temperature, furthermore, higher compressive strength of 2625 MPa and better compressive ratio of 58.8% at 600℃. CSD alloy with a refined lamellar structure exhibits higher tensile and compressive properties and better plastic strain ability than that of IM alloy. CSD alloy also has a better fracture toughness of 23.6 MPa √<m> at RT, however, the IM alloy with coarse lamellar structure exhibits higher fracture toughness of 25.34 MPa √<m> at RT, and 31.5 MPa √<m> at 800℃.
収録刊行物
-
- Proceedings of the Asian Pacific Conference on Fracture and Strength and International Conference on Advanced Technology in Experimental Mechanics
-
Proceedings of the Asian Pacific Conference on Fracture and Strength and International Conference on Advanced Technology in Experimental Mechanics 2.01.03 (0), 918-922, 2001
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206069596800
-
- NII論文ID
- 110002498246
-
- ISSN
- 24331279
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可