- K-0530 High Temperature Fatigue Strength of Ni-based Single-Crystalline Superalloy, CMSX-2
抄録
A nickel-based single-crystalline superalloy, CMSX-2 was investigated from the standpoint of high temperature fatigue strength. Three kinds of push-pull fatigue tests were conducted at 1000℃: (1) PP-test under a sinusoidal stress waveform of 1 Hz-frequency at stress amplitude of 300MPa, the number of cycles to rupture, N_f=8,234, (2) CC-test under a trapezoidal one with hold time in tension and compression of 600s each at stress amplitude of 250MPa, N_f=93, and (3) PP_<preCC>-test, which is PP-test carried out after removal of surface oxide film and small cracks generating during preceding CC-test for 47 cycles, N_f=4,318. A distinguished microstructural difference between PP and PP_<preCC> is that γ'-phase kept the initial cubic shape in PP but it changed to spherical in PP_<preCC>-Nearly 10%-increase in total strain range and 50%-decrease in fatigue life of PP_<preCC> as compared with pure PP-fatigue is attributable to the collapse of γ'-phase.
収録刊行物
-
- 年次大会講演論文集
-
年次大会講演論文集 I.01.1 (0), 185-186, 2001
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681042859264
-
- NII論文ID
- 110002526300
-
- ISSN
- 24331325
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可