In general, structural integrity depends on material performance under cyclic loading. It is therefore very important to characterize the fatigue strength characteristics of ceramic/metal joints for wide use in structural applications of engineering ceramics. In this work, in order to clarify the strength characteristics of alumina joints, static strength and cyclic fatigue tests were carried out for joints of Al2O3/Al2O3 and Al2O3/Mo/SUS 304/Mo/Al2O3 formed with Ticusil and Cu80 Ti20 fillers in vacuum. Static tests were conducted at room temperature and elevated temperature. Fatigue tests were conducted at constant stress ratio R(=0.1) and constant frequency f(=50Hz) at room temperature. The strength characteristics of the joints of Al2O3/Al2O3 formed using Ticusil were similar to the strength characteristics of Al2O3. The strength characteristics of the joints of Al2O3/Mo/SUS 304/Mo/Al2O3 were mainly determined by those of the joint of Mo/Al2O3.
収録刊行物
-
- JSME international journal. Ser. A, Mechanics and material engineering
-
JSME international journal. Ser. A, Mechanics and material engineering 39 (4), 613-619, 1996-10-15
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680409778176
-
- NII論文ID
- 110002964504
-
- NII書誌ID
- AA10888746
-
- ISSN
- 13408046
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可