Lattice Parameter Changes of Leucite by Incorporation of Various Cations Substituted for Potassium.
-
- BAN Seiji
- Department of Dental Material Science, School of Dentistry, Aichi-Gakuin University
-
- MATSUO Kenji
- Department of Dental Material Science, School of Dentistry, Aichi-Gakuin University
-
- IWASE Haruhiko
- Department of Dental Material Science, School of Dentistry, Aichi-Gakuin University
-
- KAIKAWA Kentaro
- Department of Dental Material Science, School of Dentistry, Aichi-Gakuin University
-
- HASEGAWA Jiro
- Department of Dental Material Science, School of Dentistry, Aichi-Gakuin University
この論文をさがす
抄録
Leucite crystals having modified compositions from stoichiometry were prepared by the incorporation of Na+, Rb+, Cs+, Ca2+, Ba2+, and Sb3+ substituted for 5-50 at% of K+ in the leucite. The lattice parameters of the a- and c-axes of these tetragonal leucite were derived from the diffraction angles of (400) and (004) peaks due to tetragonal leucite, respectively. Both lattice parameters of the a- and c-axes of the leucites except Rb and Cs were slightly smaller than those of stoichiometric leucite. The lattice parameters of the a-axis of the leucites containing Rb and Cs were larger than those of stoichiometric leucite (p<0.01) and increased with the content of Rb and Cs. It was concluded that the crystal lattice of leucite was deformed by the incorporation of cations substituted for K and their variations mainly depend upon the kind of cation, namely ionic size and substitution site in the lattice.
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 18 (4), 385-394, 1999
一般社団法人 日本歯科理工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204717220864
-
- NII論文ID
- 110002983516
-
- NII書誌ID
- AA10443149
-
- ISSN
- 18811361
- 02874547
-
- PubMed
- 10786159
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- PubMed
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可