Ceramic Bonding Strength of Au-1.6wt% Ti Alloy
-
- ITO Masayuki
- Division of Fixed Prosthodontics, Graduate School of Dentistry, Tohoku University
-
- KIKUCHI Masafumi
- Division of Dental Biomaterials, Graduate School of Dentistry, Tohoku University
-
- OKUNO Osamu
- Division of Dental Biomaterials, Graduate School of Dentistry, Tohoku University
-
- KIMURA Kohei
- Division of Fixed Prosthodontics, Graduate School of Dentistry, Tohoku University
Bibliographic Information
- Other Title
-
- On transcendency of special values of arithmetic automorphic functions
Search this article
Abstract
The aim of this investigation was to evaluate the metal-ceramic bonding of Au-1.6wt%Ti alloy. Therefore, the coefficient of thermal expansion, modulus of elasticity, ceramic bonding strength, and hardness of Au-1.6wt%Ti alloy were measured. The metal-ceramic interface was observed by EPMA to investigate its bonding mechanism. The Au-1.6wt%Ti alloy showed a coefficient of thermal expansion close to that of conventional precious metal alloys for metal-ceramics. Bonding strength was 25MPa or higher for all specimens—whether ceramic-fired directly after casting, or following oxidation treatment or age hardening. Specimens subjected to oxidation treatment showed slightly lower post-firing hardness than those age-hardened. EPMA observation showed an accumulation of Ti and O contents on the alloy side at the metal-ceramic interface.
Journal
-
- Dental Materials Journal
-
Dental Materials Journal 24 (2), 268-274, 2005
The Japanese Society for Dental Materials and Devices
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679693185664
-
- NII Article ID
- 110002983753
- 130000824437
-
- NII Book ID
- AA0070177X
-
- COI
- 1:CAS:528:DC%2BD2MXhtVWqsrbI
-
- ISSN
- 18811361
- 18811167
- 18812333
- 02874547
- 00255645
- http://id.crossref.org/issn/00255645
-
- NDL BIB ID
- 7668105
-
- PubMed
- 16022450
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- PubMed
- NDL-Digital
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed