Rare Earth Oxide-containing Fluorescent Glass Filler for Composite Resin
-
- UO Motohiro
- Division of Biomedical, Dental Materials and Engineering, Department of Oral Health Science, Graduate School of Dental Medicine, Hokkaido University
-
- OKAMOTO Mayumi
- Division of Oral Functional Prosthodontics, Department of Oral Functional Science, Graduate School of Dental Medicine, Hokkaido University
-
- WATARI Fumio
- Division of Biomedical, Dental Materials and Engineering, Department of Oral Health Science, Graduate School of Dental Medicine, Hokkaido University
-
- TANI Kazutoshi
- Division of Preventive Dentistry, Department of Oral Health Science, Graduate School of Dental Medicine, Hokkaido University
-
- MORITA Manabu
- Division of Preventive Dentistry, Department of Oral Health Science, Graduate School of Dental Medicine, Hokkaido University
-
- SHINTANI Akira
- OptoElectronics Department, Toyoda Gosei Co. Ltd. Present address: Koha Co. Ltd.
この論文をさがす
抄録
In recent dental care, esthetic restorative materials such as composite resin and porcelain have been widely used and studied. However, their good esthetics makes the visual inspection of restored teeth difficult. In this study, a fluorescent glass filler containing rare earth oxides—which are well-known fluorescent materials—was prepared and used in composite resin to enhance visual inspection capability with small change in color. For example, when irradiated with near ultraviolet light, an Eu2O3-containing filler fluoresced clearly and visibly. The fluorescence intensity of the prepared composite resin increased with increase of Eu2O3 content in the glass filler and with filler/resin ratio in the resin. Despite the clear fluorescence, the effect of Eu2O3 on the color change of composite resin was quite small—even when up to 10wt% Eu2O3 was added to the glass filler. Tb4O7- and Dy2O3-added fillers also showed clear fluorescence, just like Eu2O3-added filler. Therefore, fluorescent glass fillers for composite resins, resulting in small color change in the latter, were successfully prepared in this study.
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 24 (1), 49-52, 2005
一般社団法人 日本歯科理工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679693144320
-
- NII論文ID
- 110002983792
-
- NII書誌ID
- AA10443149
-
- COI
- 1:CAS:528:DC%2BD2MXks1SltLw%3D
-
- ISSN
- 18811361
- 02874547
- http://id.crossref.org/issn/02874547
-
- HANDLE
- 2115/16977
-
- PubMed
- 15881207
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- Crossref
- PubMed
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可