可視光線重合型含フッ素系軟質レジンに関する研究(第2報) : α-フルオロアクリル酸フルオロアルキルモノマーの検討  [in Japanese] Study on Visible-light Curing Soft Resins Consisting of Fluoropolymers(Part 2) : Effect of Fluoroalkyl α-Fluoroacrylate Monomers  [in Japanese]

Access this Article

Search this Article

Author(s)

    • 大江 陽一郎 OHE Yohichiro
    • 東京医科歯科大学医用器材研究所機能性高分子部門 Division of Functional Polymer, Institute for Medical and Dental Engineering, Tokyo Medical and Dental University
    • 門磨 義則 KADOMA Yoshinori
    • 東京医科歯科大学医用器材研究所機能性高分子部門 Division of Functional Polymer, Institute for Medical and Dental Engineering, Tokyo Medical and Dental University
    • 今井 庸二 IMAI Yohji
    • 東京医科歯科大学医用器材研究所機能性高分子部門 Division of Functional Polymer, Institute for Medical and Dental Engineering, Tokyo Medical and Dental University

Abstract

フッ素系ポリマーであるフッ化ビニリデン, ヘキサフルオロプロピレンよりなる共重合体(2-6F), またはフッ化ビニリデン, テトラフルオロエチレン, ヘキサフルオロプロピレンよりなる共重合体(2-4-6F)と, 2, 2, 3, 3-テトラフルオロプロピルα-フルオロアクリレート(4FFA), 2, 2, 3, 3, 3-ペンタフルオロプロピルα-フルオロアクリレート(5FFA), 2, 2, 3, 3, 4, 4, 5, 5-オクタフルオロペンチルα-フルオロアクリレート(8FFA), 2, 2, 3, 3, 4, 4, 5, 5, 6, 6, 7, 7-ドデカフルオロヘプチルα-フルオロアクリレート(12FFA)を組み合わせた新しい可視光線重合型の軟質レジンを試作し, 軟質裏装材料としての応用を考慮しつつその理工学的性質を検討した.水に対する接触角は, 4FFAで85〜90°, 8FFAで90〜93°, 12FFAで92〜93°であり, フッ素原子をより多く導入するにつれて高くなった.-CF_3基を含む5FFAでは95〜96°と相対的により高くなった.硬さは2-4-6F系で軟化傾向が認められ, 8FFAとの組合せが最も軟らかく, 硬度(JIS A)43〜46と十分な軟らかさとなった.10週間の真の吸水率は, 4FFAと2-6Fで0.4〜0.9%と最小となり, 最大でも8FFAと2-4-6Fの2%程度であり, かなり小さかった.溶解率は, 4FFAで最も少なく0.2〜0.4%, 8FFA, 12FFAで1.0〜1.4%となった.モノマー溶出率は最大でも12FFAの0.4%であり小さかった.以上のように, 前回改善の必要が認められた硬さ, 吸水率が大幅に改善され, 現在市販されている軟質材料と比較してもかなり優れた性質のものが得られた.

New experimental visible-light cured soft resins were prepared by combining a vinylidene fluoride/hexafluoropropylene copolymer(2-6F), or a vinylidene fluoride/tetrafluoroethylene/hexafluoropropylene copolymer(2-4-6F)with 2, 2, 3, 3-tetrafluoropropyl α-fluoroacrylate(4FFA), 2, 2, 3, 3, 3-pentafluoropropyl α-fluoroacrylate(5FFA), 2, 2, 3, 3, 4, 4, 5, 5-octafluoropentyl α-fluoroacrylate(8FFA), or 2, 2, 3, 3, 4, 4, 5, 5, 6, 6, 7, 7-dodecafluoroheptyl α-fluoroacrylate(12FFA).Some properties of the resins prepared were measured to determine whether they would be candidate materials for the soft denture liner.Water contact angles increased with the increase in the number of fluorine atoms contained in the monomers:85〜90° in 4FFA, 90〜93° in 8FFA, and 92〜93° in 12FFA.Softer resins were obtained with 2-4-6F, especially by the combination with 8FFA giving the softest resin with a hardness of 43〜46(JIS A).Water sorption after 10 weeks was considerably low:0.4〜2%:0.4〜0.9% in 4FFA/2-6F and about 2% in 8FFA/2-4-6F.Solubility was 0.2〜0.4% in the resins with 4FFA and 1.0〜1.4% with 8FFA or 12FFA.Amount of residual monomer was low, and the maximum was 0.4% in the resin with 12FFA.Thus hardness and water sorption of the resins prepared were superior to those of the commercial soft materials.

Journal

  • The Journal of the Japanese Society for Dental Materials and Devices

    The Journal of the Japanese Society for Dental Materials and Devices 9(4), 647-653, 1990

    The Japanese Society for Dental Materials and Devices

Cited by:  4

Codes

  • NII Article ID (NAID)
    110002996243
  • NII NACSIS-CAT ID (NCID)
    AN00127279
  • Text Lang
    JPN
  • Article Type
    Journal Article
  • ISSN
    0286-5858
  • Data Source
    CJPref  NII-ELS  J-STAGE 
Page Top