非金属介在物の水素トラップ効果に対する検討
書誌事項
- タイトル別名
-
- Effect of Nonmetallic Inclusions on Weld Cold Cracking (Report 3) : Investigation on the Trapping Effect of Inclusions on Hydrogen Diffusion (Papers Submitted to National Meeting Autumn 1985)
この論文をさがす
抄録
In this work, the trapping effect of inclusions on hydrogen diffusion was investigated and it was considered how this trapping effect affected on hydrogen embrittlement. The results in this work were as follows ;(1) At room temperature diffusion coefficients were lowered and nondiffusible hydrogen contents were increased with increasing inclusions. Therefore, it was aquired that inclusions acted as both reversible and irreversible trapping sites in steels.(2) It was appeared that nondiffusible hydrogen was trapped in inclusions and microvoids produced at inclusions at room temperature.(3) It was appeared by measurement of binding energy between trapping sites and hydrogen that reversible trapping effect of inclusions on hydrogen diffusion was caused by dislocation fields developed around inclusions during oil quenching of steels.(4) It was concluded by considering the model of hydrogen embrittlement proposed by Beachem that the index of hydrogen embrittlement was relative to concentration of hydrogen at the crack tip. And it was appeaered that inclusions lowered the concentration of hydrogen, thus elevated K_<TH>.(5) K_<TH> values were elevated by Ce treatment, while diffusivity of hydrogen was not affected by Ce treatment. The reason of this result was caused by the upward shift of critical line in Beachem model because of higher K_<IC> of Ce treated steel.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 3 (3), 490-497, 1985
社団法人溶接学会
- Tweet
キーワード
詳細情報
-
- CRID
- 1570572702415846784
-
- NII論文ID
- 110003422541
-
- NII書誌ID
- AN1005067X
-
- ISSN
- 02884771
-
- 本文言語コード
- ja
-
- データソース種別
-
- CiNii Articles