Corrosion Characteristics of .ALPHA.-Ti and Ti2Cu Composing Ti-Cu Alloys
-
- TAKADA Yukyo
- Division of Dental Biomaterials, Graduate School of Dentistry, Tohoku University
-
- OKUNO Osamu
- Division of Dental Biomaterials, Graduate School of Dentistry, Tohoku University
Bibliographic Information
- Other Title
-
- Corrosion characteristics of α-Ti and Ti2Cu composing Ti-Cu alloys
Search this article
Abstract
A series of binary Ti-Cu alloys containing 5-20 mass% Cu was prepared, and the corrosion behavior of α-Ti and Ti2Cu composing the Ti-Cu alloys were examined based on the anodic polarization curves and released ions in 0.9% NaCl and 1% lactic acid solutions. In both solutions, the Ti-Cu alloys showed the same anodic polarization curves as titanium in the condition below 1.4 V. However, precipitation of Ti2Cu contributed to a small increase in current densitiy in the transpassive region beyond 1.4 V. The amount of Cu ions released from Ti2Cu was 0.260 and 1.003 (μg/cm2/7 days) in 0.9% NaCl and 1% lactic acid solutions respectively. Although these values were larger than those from α-Ti (0.0379±0.0041 and 0.0962±0.0327 (μg/cm2/7days) in NaCl and lactic acid solutions respectively), they were not greater than those from type 4 gold alloy under the same conditions.
Journal
-
- Dental Materials Journal
-
Dental Materials Journal 24 (4), 610-616, 2005
The Japanese Society for Dental Materials and Devices
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679692226688
-
- NII Article ID
- 110003495348
-
- NII Book ID
- AA10443149
-
- COI
- 1:CAS:528:DC%2BD28XitFWis7w%3D
-
- ISSN
- 18811361
- 02874547
- http://id.crossref.org/issn/02874547
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- NDL-Digital
- CiNii Articles
-
- Abstract License Flag
- Disallowed