コンクリートの破壊挙動に及ぼす粗骨材の影響 : 第 1 報 : モデル解析法による検討

DOI Web Site Web Site 被引用文献9件

書誌事項

タイトル別名
  • EFFECT OF COARSE AGGREGATE ON FRACTURE OF CONCRETE : Part 1 : Model Analysis
  • コンクリートの破壊挙動に及ぼす粗骨材の影響-1-モデル解析法による検討
  • コンクリート ノ ハカイ キョドウ ニ オヨボス ソコツザイ ノ エイキョウ

この論文をさがす

抄録

The purpose of this investigation is to examine the effect of the strength and surface condition of coarse aggregate on the fracture of concrete under uniaxial compression. The two-phase model specimens consisted of a cylindrical coarse aggregate and mortar matrix were used to simplify the study. Three kinds of compressive strength and five kinds of surface condition were provided for coarse aggregates. The following conclusions were obtained by this investigation. 1) Regardless of the surface roughness of aggregate, the fracture process of model concrete with an aggregate whose compressive strength (Fca) is smaller than that of mortar matrix (Fcm) was as follows; (1) initiation of bond crack between aggregate and mortar matrix, (2) tensile cracking of mortar matrix and aggregate parallel to the longitudinal axis, (3) local compressive failure of aggregate and (4) failure of model concrete. 2) The fracture process of model concrete with an aggregate whose strength is larger than that of mortar matrix was as follows; (1) initiation of bond crack, (2) tensile cracking of mortar matrix, (3) local compressive failure of mortar matrix at the vicinity of aggregate and (4) failure of model concrete. 3) The compressive strength (Fcc) of model concrete increases with the increase of the value of Fca in the range of Fca/Fcm<1, but never increases in the range of Fca/Fcm>1, regardless of the surface ronghness of coarse aggregate.

収録刊行物

被引用文献 (9)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ