超音波疲労試験によるオーステナイト系ステンレス鋼の超高サイクル疲労強度評価  [in Japanese] Evaluation of Giga-cycle Fatigue Properties of Austenitic Stainless Steels Using Ultrasonic Fatigue Test  [in Japanese]

Access this Article

Search this Article

Author(s)

Abstract

Ultrasonic fatigue tests have been performed in austenitic stainless steel, SUS 316 NG, in order to investigate giga-cycle fatigue strength of pre-stained materials, i.e. 5, 10 and 20% tensile pre-strains and -20% compressive pre-strain. The pre-strains were applied before specimen machining. The austenitic stainless steels are known to exhibit remarkable self-heating during the fatigue experiment. Therefore, heat radiation method was established by setting fatigue specimens in a low temperature chamber at about -100°C. The self-heating was controlled by intermittent loading condition, which enabled us to maintain the test section of the specimens at about room temperature. The results revealed that the fatigue strength increased with increasing pre-strain levels. Fish eye fracture was observed for -20% pre-strained specimen fractured at 4.11×10<SUP>7</SUP> cycles, while the other specimens exhibited ordinary fatigue fracture surface originated from stage I facet on the specimen surface. The increase in fatigue limit was predicted by Vickers hardness, <I>HV</I>, which depended on the size of indented region. The prediction was successful using <I>HV</I> values obtained by the size of the indented region similar to those of the stage I facets.

Journal

  • TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A

    TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A 72(723), 1731-1736, 2006-11-25

    The Japan Society of Mechanical Engineers

References:  10

Cited by:  3

Codes

  • NII Article ID (NAID)
    110004997340
  • NII NACSIS-CAT ID (NCID)
    AN0018742X
  • Text Lang
    JPN
  • Article Type
    Journal Article
  • ISSN
    03875008
  • NDL Article ID
    8589803
  • NDL Source Classification
    ZM16(科学技術--科学技術一般--工業材料・材料試験)
  • NDL Call No.
    Z14-737
  • Data Source
    CJP  CJPref  NDL  NII-ELS  J-STAGE 
Page Top