書誌事項
- タイトル別名
-
- Effects of Stress Ratio on Surface- and Interior-Originating Fatigue Properties of High Strength Steel
- コウキョウド コウ ノ ヒョウメン オヨビ ナイブ キテンガタ ヒロウ トクセイ ニ オヨボス オウリョクヒ ノ エイキョウ
この論文をさがす
抄録
In order to clarify effects of stress ratios (R=σmin/σmax) on surface- and interior-originating fatigue properties, uniaxial fatigue tests of high strength steel (SNCM 439) were carried out under three different stress ratios, R=0.3, 0.1 and -1. Based on tests results and fractographic analysis in initial crack propagation regions (Optically Dark Area (ODA) and Stage 2 a), the following results were obtained, (1) Surface-originating fractures occurred in the same fatigue life region regardless of the stress ratio. On the other hand, interior-originating fractures occurred at a longer fatigue life region, as the stress ratio increased. It is unsure to apply the modified Goodman diagram to high strength steels of which main fracture mode was the interior-originating fracture. (2) In initial crack propagation regions, the fracture surface of the interior-originating fracture was strongly affected by the stress ratio, even though that of the surface-originating fracture was scarcely affected. The formation of a fine bumpy pattern which was characteristic of the ODA's fracture surface was affected by a multiplier effect of the inner environment of material and the compression load.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 70 (696), 1042-1049, 2004
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679456150272
-
- NII論文ID
- 110004998797
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL書誌ID
- 7077050
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可