Hydrogen Storage in Amorphous Phase of Hydrogenated Carbon Nitride.

• Ohkawara Yoshiaki

  Nagaoka University of Technology, Kamitomioka, Nagaoka, Niigata 940-2188, Japan

• Ohshio Shigeo

  Nagaoka University of Technology, Kamitomioka, Nagaoka, Niigata 940-2188, Japan

• Suzuki Tsuneo

  Nagaoka University of Technology, Kamitomioka, Nagaoka, Niigata 940-2188, Japan

• Yatsui Kiyoshi

  Nagaoka University of Technology, Kamitomioka, Nagaoka, Niigata 940-2188, Japan

• Ito Haruhiko

  Nagaoka University of Technology, Kamitomioka, Nagaoka, Niigata 940-2188, Japan

• Saitoh Hidetoshi

  Nagaoka University of Technology, Kamitomioka, Nagaoka, Niigata 940-2188, Japan

抄録

A hydrogen storage characteristic of amorphous phase of hydrogenated carbon nitride (a-CN_x:H) was evaluated at room temperature under high-pressure hydrogen. The hydrogen content in the sample was directly measured using a volumetric analysis established for measuring the hydrogen adsorption of metal alloys. The content of stored hydrogen in a-CN_x:H was twice as much as those of multiwalled nanotubes, charcoal activated powder and carbon fiber.

収録刊行物

• Japanese Journal of Applied Physics

  Japanese Journal of Applied Physics 41 (12), 7508-7509, 2002

  The Japan Society of Applied Physics

キーワード

• hydrogen storage
• carbon nitride
• ERDA

詳細情報

• CRID: 1390001206256994176
• NII論文ID: 110006342189
• NII論文ID: 210000052429
• NII論文ID: 130004529223
• NII書誌ID: AA10457675
• DOI: 10.1143/jjap.41.7508
• ISSN: 13474065
• ISSN: 00214922
• Web Site: http://stacks.iop.org/1347-4065/41/i=12R/a=7508/pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可