Twenty-four Hour Flexural and Shear Bond Strengths of Flowable Light-cured Composites: A comparison Analysis Using Weibull Statistics
-
- TJANDRAWINATA Rosalina
- Department of Dental Materials, Faculty of Dentistry, Trisakti University, Campus B
-
- IRIE Masao
- Department of Biomaterials, Okayama University Graduate School of Medicine, Dentistry and Pharmaceutical Science
-
- SUZUKI Kazuomi
- Department of Biomaterials, Okayama University Graduate School of Medicine, Dentistry and Pharmaceutical Science Research Center for Biomedical Engineering, Okayama University
この論文をさがす
抄録
By means of Weibull analysis, this study evaluated and compared the flexural strength and shear bond strength of flowable light-cured composites against those of conventional ones. Twenty specimens of each material were prepared for flexural and shear bond strength measurements. Specimens were measured after water storage at 37°C for 24 hours. Three of four flowable composites showed significantly higher flexural strength than conventional ones, with Weibull moduli ranging between 6 and 14. With the presence of a bonding agent, the shear bond strength to enamel of both types was not different significantly (p=0.28), with Weibull moduli ranging between 4 and 9. In the selection of an excellent resin composite material, results of this study showed that a high, stable Weibull modulus value could be a sound indicator.
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 26 (4), 589-597, 2007
一般社団法人 日本歯科理工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679693348736
-
- NII論文ID
- 110006368721
-
- NII書誌ID
- AA10443149
-
- COI
- 1:STN:280:DC%2BD2srmvVSquw%3D%3D
-
- ISSN
- 18811361
- 02874547
-
- PubMed
- 17886465
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- PubMed
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可