Electrophoretic Deposition Zirconia/Alumina of Ceria-stabilized Zironia/Alumina Powder
-
- NAKAMURA Takashi
- Department of Fixed Prosthodontics, Osaka University Graduate School of Dentistry
-
- NISHIDA Hisataka
- Department of Operative Dentistry, Osaka Dental University
-
- SEKINO Tohru
- Institute of Scientific and Industrial Research, Osaka University
-
- NAWA Masahiro
- Matsushita Electric Works Ltd.
-
- WAKABAYASHI Kazumichi
- Department of Fixed Prosthodontics, Osaka University Graduate School of Dentistry
-
- KINUTA Soichiro
- Department of Fixed Prosthodontics, Osaka University Graduate School of Dentistry
-
- MUTOBE Yoshihiko
- Department of Fixed Prosthodontics, Osaka University Graduate School of Dentistry
-
- YATANI Hirofumi
- Department of Fixed Prosthodontics, Osaka University Graduate School of Dentistry
Search this article
Abstract
The aim of this study was to evaluate the electrophoretic deposition (EPD) behavior of ceria-stabilized zirconia/alumina (Ce-TZP/Al2O3) granulated powder. Two types of slurry with powder-to-solvent ratios of 10 wt% and 20 wt% were used. Zeta potential of the slurries was measured using a spectrometer at different pH levels. Then, EPD was performed to measure the weight of the deposited particles at varying pH levels and at two voltages (50 V and 100 V). The isoelectric point of Ce-TZP/Al2O3 mixed powder was approximately at pH 8.5. When EPD was performed, deposition of ceramic particles was typically observed in the range of pH 3 to pH 7, with the greatest deposition found at around pH 7. Moreover, the deposition of ceramic particles increased with increase in slurry concentration and voltage.
Journal
-
- Dental Materials Journal
-
Dental Materials Journal 26 (5), 623-627, 2007
The Japanese Society for Dental Materials and Devices
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204715452928
-
- NII Article ID
- 110006402819
-
- NII Book ID
- AA10443149
-
- COI
- 1:CAS:528:DC%2BD2sXhsVKns7rO
-
- ISSN
- 18811361
- 02874547
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- NDL-Digital
- CiNii Articles
-
- Abstract License Flag
- Disallowed