3623 ショットピーニングしたアルミニウム合金の疲労強度に及ぼす表面粗さの影響(G03-3 表面改質,G03 材料力学)

• 本田 尚

  産安研

• 山口 篤志

  東電大

• KOBAYASHI Albert S.

  ワシントン大学

• RAMULU Mamidala

  ワシントン大学

書誌事項

タイトル別名

• 3623 Effect of Surface Roughness on Fatigue strength of Shot Peened Aluminum Alloy

抄録

The objective of this research was to determine the effect of surface roughness on fatigue strength in peened 7075-T7351 three point bend (TPB) specimens. Surface roughness of as-received and peened specimens (with four Almen scales (4, 8, 12, 16)) was measured with the laser microscope. All specimens were fatigued to failure at various stress levels, and a S-N diagram was constructed. The fatigue strength of 7075-T7351 was improved by shot peening, and the effect of shot peening on fatigue strength was inversely proportional to the shot intensity. Since the surface roughness in peened TPB specimens was proportional to shot intensity, the fatigue limits of peened specimens were evaluated by equivalent defect size √<area_R>, which is applied to irregularly shaped surface roughness. The fatigue limits evaluated by √<area_R> were agreed with experimental results well.

収録刊行物

• 年次大会講演論文集

  年次大会講演論文集 2006.1 (0), 783-784, 2006

  一般社団法人 日本機械学会

キーワード

• Fatigue
• Surface Roughness
• Stress Intensity Factor
• Shot peening
• Residual Stress

詳細情報

• CRID: 1390282681037890816
• NII論文ID: 110006634643
• DOI: 10.1299/jsmemecjo.2006.1.0_783
• ISSN: 24331325
• Web Site: https://www.jstage.jst.go.jp/article/jsmemecjo/2006.1/0/2006.1_783/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可