B121 PEFC劣化機構解明のための排ガス中微量成分in-line計測(分散エネルギーシステムにおける要素技術とその集積化2)

• 藤井 義喜

  東工大院

• 津島 将司

  東工大

• 平井 秀一郎

  東工大

書誌事項

タイトル別名

• B121 Inline mass spectroscopic analysis in exhaust gas for investigation of PEFC degradation

抄録

In-line direct gas mass spectroscopy (DGMS) was applied for real-time monitoring of exhausted gas of a polymer electrolyte fuel cell (PEFC) in order to investigate degradation behaviors of the fuel cell. It was shown that hydrogen emission in cathode exhausted gas was larger under OCV operation than load operation, and that intermittent peaks of carbon dioxide emission in cathode exhausted gas were detected with positive sweep of cell potential, suggesting that carbon corrosion of the cathode catalyst proceed under load cycle operation.

収録刊行物

• 熱工学コンファレンス講演論文集

  熱工学コンファレンス講演論文集 2006 (0), 45-46, 2006

  一般社団法人 日本機械学会

キーワード

• PEFC
• Degradation
• DGMS
• In-line

詳細情報

• CRID: 1390282680858180224
• NII論文ID: 110006637793
• DOI: 10.1299/jsmeted.2006.45
• ISSN: 2424290X
• Web Site: https://www.jstage.jst.go.jp/article/jsmeted/2006/0/2006_45/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可