Flexural Performance of Flowable versus Conventional Light-cured Composite Resins in a Long-term in vitro Study
-
- IRIE Masao
- Department of Biomaterials, Okayama University Graduate School of Medicine, Dentistry and Pharmaceutical Science
-
- TJANDRAWINATA Rosalina
- Department of Dental Materials Faculty of Dentistry, Trisakti University
-
- E Lihua
- Department of Orthodontics and Dentofacial Orthopedics, Okayama University Graduate School of Medicine, Dentistry and Pharmaceutical Science
-
- YAMASHIRO Takashi
- Department of Orthodontics and Dentofacial Orthopedics, Okayama University Graduate School of Medicine, Dentistry and Pharmaceutical Science
-
- SUZUKI Kazuomi
- Department of Biomaterials, Okayama University Graduate School of Medicine, Dentistry and Pharmaceutical Science Research Center for Biomedical Engineering, Okayama University
Search this article
Abstract
The purpose of this study was to evaluate the flexural strength, flexural modulus, modulus of resilience, and water sorption of four flowable light-cured composite resins (FCRs). Results were then compared with four conventional composite resins (CCRs) and a minifilled hybrid light-cured composite resin, which served as a control. Twenty specimens were flexural tested immediately after curing, while others were stored in water at 37°C for 1 month, 3 months, 6 months, or 1 year before flexural testing. The 1-year specimens were weight-measured at designated time intervals to examine water sorption. All FCRs, except Point 4 Flowable, showed higher flexural strength values than their CCR counterparts (p<0.05, Scheffé's test). After one-year water storage, the flexural strengths and flexural moduli of FCRs increased 1.5-fold or more when compared with the immediate condition. In most cases, the moduli of resilience of FCRs were higher than those of CCRs. In conclusion, it was found that FCR and CCR with the same brand name had very different characteristics and mechanical properties.
Journal
-
- Dental Materials Journal
-
Dental Materials Journal 27 (2), 300-309, 2008
The Japanese Society for Dental Materials and Devices
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679694619392
-
- NII Article ID
- 110006649463
-
- NII Book ID
- AA10443149
-
- COI
- 1:STN:280:DC%2BD1czntlSrtQ%3D%3D
-
- ISSN
- 18811361
- 02874547
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- NDL-Digital
- CiNii Articles
-
- Abstract License Flag
- Disallowed