アルミナの粒子成長速度に対する気孔の影響

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • The Effect of Pores on the Grain Growth Rate of Sintered Alumina
  • アルミナ ノ リュウシ セイチョウ ソクド ニ タイスル キコウ ノ エイキョウ
  • Studies on Sintering of Alumina, III
  • アルミナの焼結に関する研究 (第3報)

この論文をさがす

抄録

The effect of pores on the grain growth rate of alumina was investigated using specimens of various green densities in the range from 20 to 94% of theoretical one, which were prepared in four different methods in graphite molds, a) hot-pressing at 1600°C, b) hot-pressing at 1200°C, c) pressing at a room temperature and d) filling at a room temperature. After the forming pressure was removed graphite molds were heated inductively up to 1800°, 1850° or 1900°C and kept at the temperatures for 5, 10 or 60 min. The forming and heating atmosphere was a mixture of nitrogen and carbon monooxide gas.<br>By these experiments the rate of grain growth: dD/dt, the average grain diameter: D, and the volume fraction of pores: f and the average diameter of pores: d, were determined. Among them next relationship was found to exist:<br>dD/dt=K(1/D-2f/d)<br>The same experiments as above were carried out with 0.16% addition of magnesia, and the significant retarding effect of magnesia on the grain growth of alumina was observed. In this case next relationship was found to exist:<br>dD/dt=K(1/D-2f/d-K′)<br>K′ represents the retarding effect of magnesia, the value of which was found to be constant among specimens of the same heating temperature and time, and larger than the value of 2f/d corresponding to 16 vol.% of pores.<br>The exponent of time, m, in the equation D2-D02=ktm was found to increase with decreasing green density of specimens.<br>The growth of pores in specimens was observed and added magnesia was found also to have an effect on the pore growth.

収録刊行物

  • 窯業協會誌

    窯業協會誌 72 (822), 104-109, 1964

    公益社団法人 日本セラミックス協会

被引用文献 (1)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ