Effect of Diameter of Glass Fibers on Flexural Properties of Fiber-reinforced Composites
-
- OBUKURO Motofumi
- Division of Removable Prosthodontics, Fukuoka Dental College
-
- TAKAHASHI Yutaka
- Division of Removable Prosthodontics, Fukuoka Dental College
-
- SHIMIZU Hiroshi
- Division of Removable Prosthodontics, Fukuoka Dental College
この論文をさがす
抄録
This study investigated the effect of the diameter of glass fibers on the flexural properties of fiber-reinforced composites. Bar-shaped test specimens of highly filled fiber-reinforced composites (FRCs) and FRC of 30 vol% fiber content were made from a light-cured dimethacrylate monomer liquid (mixture of urethane dimethacrylate and triethylene glycol dimethacrylate) with silanized E-glass fibers (7, 10, 13, 16, 20, 25, 30, and 45 μm in diameter). Flexural strength and elastic modulus were measured. The flexural strength of the highly filled FRCs increased with increasing fiber diameter. In particular, the strengths of highly filled FRCs with 20-, 25-, 30-, and 45-μm-diameter fibers was significantly higher than the others (p<0.05). The flexural strength of FRC of 30 vol% fiber content increased with increasing fiber diameter, except for the FRC with 45-μm-diameter fibers; FRCs with 20-, 25-, and 30-μm-diameter fibers were significantly stronger than the others (p<0.05). Therefore, it was revealed that the diameter of glass fibers significantly affected the flexural properties of fiber-reinforced composites.
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 27 (4), 541-548, 2008
一般社団法人 日本歯科理工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204716326656
-
- NII論文ID
- 110006861863
-
- NII書誌ID
- AA10443149
-
- COI
- 1:STN:280:DC%2BD1cnktlahsg%3D%3D
-
- ISSN
- 18811361
- 02874547
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可