フッ化ジアミンシリケートの象牙質知覚過敏症治療剤への応用 : 抜去歯を用いた象牙細管封鎖能の検討 Application of Ammonium Hexafluorosilicate for the Treatment of Dentin Hypersensitivity : Evaluation of Occluding Ability of Dentin Tubules Using Human Extracted Teeth

この論文にアクセスする

この論文をさがす

著者

    • 菅 俊行 SUGE Toshiyuki
    • 徳島大学大学院ヘルスバイオサイエンス研究部発達予防医歯学部門健康長寿歯科学講座歯科保存学分野 Department of Conservative Dentistry, Institute of Health Biosciences, The University of Tokushima Graduate School
    • 石川 邦夫 ISHIKAWA Kunio
    • 九州大学大学院歯学研究院口腔機能修復学講座生体材料工学 Division of Oral Rehabilitation, Department of Biomaterials, Kyushu University Faculty of Dental Science
    • 松尾 敬志 MATSUO Takashi
    • 徳島大学大学院ヘルスバイオサイエンス研究部発達予防医歯学部門健康長寿歯科学講座歯科保存学分野 Department of Conservative Dentistry, Institute of Health Biosciences, The University of Tokushima Graduate School
    • 恵比須 繁之 EBISU Shigeyuki
    • 大阪大学大学院歯学研究科口腔分子感染制御学講座(歯科保存学教室) Department of Restorative Dentistry and Endodontology, Division of Oral Infections and Disease Control, Osaka University Graduate School of Dentistry

抄録

フッ化ジアンミン銀(サホライド®)は,齲蝕進行抑制剤および象牙質知覚過敏症治療剤として臨床で使用されている.しかしながら,フッ化ジアンミン銀は塗布後に銀の沈着による歯の黒変が起こる.したがって,フッ化ジアンミン銀は主に乳歯に使用されている.この欠点を改良するために,フッ化ジアミンシリケートを調製した.銀の代わりにシリカを導入した理由は,シリカは歯質の変色を起こさないこと,そして擬似体液からアパタイトの生成を誘導するからである.本研究の目的はヒト口腔内を模倣した環境下において,フッ化ジアミンシリケート処理後の象牙細管封鎖効果と持続性を評価することである.フッ化ジアミンシリケートの象牙細管封鎖効果は,ヒト抜去歯を用いて評価を行った.フッ化ジアミンシリケート処理直後および人工唾液浸漬7日後の象牙質プレートの表面を,走査電子顕微鏡(SEM)にて観察を行った.SEM観察の結果,開口象牙細管はフッ化ジアミンシリケート処理直後にはシリカ-リン酸カルシウム結晶により完全に封鎖されていた.さらに,人工唾液浸漬7日後には象牙質表面は新たに生成した結晶により覆われていた.EDXA分析によると,フッ化ジアミンシリケート処理直後に象牙細管内に析出した結晶はシリカ,カルシウム,リンを含有しており,シリカ-リン酸カルシウム結晶であることが明らかとなった.その結晶のカルシウムとリンのモル比はフッ化ジアミンシリケート処理直後には2.02であったが,人工唾液浸漬後には徐々に減少した.一方,象牙質表面に新たに生成した結晶は実験期間を通して,ほぼ一定の値(Ca/P=1.16〜1.28)であった.周囲の管間象牙質と比べて有意に低い値であることから,おそらくカルシウム欠損アパタイトが析出していると推察された.フッ化ジアミンシリケート処理は人工唾液中からリン酸カルシウムの析出を誘導し,したがって,ヒト口腔内を模倣した環境下において,持続的な象牙細管封鎖能を有することが明らかとなった.

Diamine silver fluoride (Saforide®) is used clinically to prevent the progress of dental caries and desensitize hypersensitive teeth. Unfortunately, diamine silver fluoride stains teeth black due to silver precipitation; therefore, it is mainly applied to deciduous teeth. To overcome this drawback, ammonium hexafluorosilicate(SiF:(NH_4)_2SiF_6)was prepared. Silica was employed instead of silver because it does not change the color of teeth, and is well known to induce apatite formation from simulated body fluids. The purpose of this study was to evaluate the occluding ability and duration of dentin tubule occlusion after SiF treatment in a simulated oral environment. The occluding ability of SiF was evaluated using human dentin disks. The surface of dentin disks was observed with a scanning electron microscope (SEM)immediately after SiF treatment and 7 days after immersion in synthetic saliva. SEM observation showed that open dentin tubules were occluded completely with silica-calcium phosphate precipitate immediately after SiF treatment. In addition, newly formed crystals covered the dentin surface 7 days after immersion in synthetic saliva. EDXA analysis showed that the precipitate formed in the dentin tubules after SiF treatment contains silica, calcium and phosphorous indicating silica-calcium phosphate complex. The Ca/P molar ratio of the precipitate formed with SiF treatment was 2.02, and the value gradually decreased after immersion in synthetic saliva. In contrast, the Ca/P molar ratio of newly formed crystals at the dentin surface showed a relatively constant value(Ca/P=1.16-1.28)throughout the experimental period. It seems that calcium-deficient apatite may be precipitated at the dentin surface due to the Ca/P ratio being significantly lower than that of intertubular dentin. SiF treatment induced calcium phosphate precipitation from synthetic saliva; therefore, it has a continuous effect on dentin tubule occlusion under a simulated oral environment.

収録刊行物

  • 日本歯科保存学雑誌

    日本歯科保存学雑誌 50(3), 313-320, 2007

    特定非営利活動法人 日本歯科保存学会

参考文献:  17件中 1-17件 を表示

被引用文献:  5件中 1-5件 を表示

各種コード

  • NII論文ID(NAID)
    110007151182
  • NII書誌ID(NCID)
    AN00191201
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    0387-2343
  • データ提供元
    CJP書誌  CJP引用  NII-ELS  J-STAGE 
ページトップへ