試作S-PRGフィラー含有根管充填用シーラーに関する研究 : 根管封鎖性,抗菌性および根管壁への各種イオンの移行について  [in Japanese] Evaluation of Selected Properties of a Prototype S-PRG Filler Containing Root Canal Sealer  [in Japanese]

Access this Article

Search this Article

Author(s)

    • 韓 臨麟 HAN Linlin
    • 新潟大学大学院医歯学総合研究科口腔健康科学講座う蝕学分野 Division of Cariology, Operative Dentistry and Endodontics, Department of Oral Health Science, Niigata University Graduate School of Medical and Dental Sciences
    • 竹中 彰治 TAKENAKA Shoji
    • 新潟大学大学院医歯学総合研究科口腔健康科学講座う蝕学分野 Division of Cariology, Operative Dentistry and Endodontics, Department of Oral Health Science, Niigata University Graduate School of Medical and Dental Sciences
    • 興地 隆史 OKIJI Takashi
    • 新潟大学大学院医歯学総合研究科口腔健康科学講座う蝕学分野 Division of Cariology, Operative Dentistry and Endodontics, Department of Oral Health Science, Niigata University Graduate School of Medical and Dental Sciences

Abstract

多機能性表面処理ガラスフィラー(Surface reaction type pre-reacted glass ionomer filler:以下,S-PRGフィラー)は,コンポジットレジンなどに配合することによりフッ素(F),ストロンチウム(Sr),ホウ素(B)などのさまざまな元素の徐放能を付与することが可能とされる.本研究では,新たに開発されたS-PRGフィラー含有試作根管充填用シーラー(以下,S-PRGシーラー,松風)の諸性質を検討した.1.歯冠側における根管封鎖性の評価 ヒト抜去単根歯20本の歯根部を試料とし,#40/.06テーパーに拡大形成後,EDTA含有根管洗浄液(スメアクリーン®,日本歯科薬品)を根管壁に作用させた.次いで無作為に4群(各n=5)に分け,S-PRGシーラー,もしくは酸化亜鉛ユージノール系シーラー(PulpDent® Root Canal Sealer:以下,PulpDentシーラー)による糊剤根管充填,もしくはガッタパーチャポイントを併用した側方加圧根管充填を行った.試料を蒸留水中に60日保管後,0.2%フクシン溶液に24時間浸漬した後,歯根横断切片の実体顕微鏡観察を行い,根管口から根尖側1,3,5mmの位置での色素浸透を5段階のスコアで評価した.2.根管壁象牙質への各種イオンの取り込み観察 色素浸透試験と同様の方法で作製した試片を,蒸留水中に7あるいは60日間保管後,根管横断面の薄切片を作製し,根管壁におけるF,Sr,Bの分布を波長分散型エックス線マイクロアナライザーにより分析した.3.抗菌性の評価 Enterococcus faecalis,Propionihacterium acnesあるいはActinomyces israeliiが培養された血液寒天平板上に,S-PRGシーラーおよびPulpDentシーラー(いずれも練和直後および練和12時間後)を静置し,37℃,24時間嫌気培養後の阻止円の形成を観察した.これらの実験より,以下の結果が得られた. 1. いずれの観察位置とも,色素浸透に4群間の有意差はみられなかった(Kruskal-Wallis検定,p>0.05). 2. S-PRGシーラーと接する根管壁象牙質に,FおよびSrの取り込みが確認された.PulpDentシーラーでは取り込みは観察されなかった. 3. 2種のシーラーは練和直後,練和12時間後ともP. acnesおよびA. israeliiに対し抗菌性を示した.E. faecalisに対する抗菌性は認められなかった.以上より,S-PRGシーラーがフッ素,ストロンチウム徐放能を備えること,および酸化亜鉛ユージノール系シーラーと同程度の根管封鎖性と抗菌性を示すことが示唆された.

The surface reaction type pre-reacted glass-ionomer (S-PRG) filler confers the ability to release fluoride and other ions when added to various filling materials including resin composites. In this study, some properties of a prototype S-PRG filler-containing root canal sealer (S-PRG sealer; Shofu Inc.) were evaluated. A zinc oxideeugenol sealer (PulpDent root canal sealer) was used as the control material. The coronal sealing ability of the test and control sealers, used with or without guttapercha points, was assessed with a dye penetration test where the penetration of basic fuchsin at 1-, 3- and 5-mm levels from the canal orifice was scored after 60 days of immersion. Distribution of F, Sr and B in the root canal wall dentin was mapped at 7 and 60 days after root canal filling by means of electron probe microanalysis. The antibacterial activity of fresh and set (12h after mixing) sealers against Enterococcus faecalis, Propionibacterium acnes and Actinomyces israelii was examined with an agar diffusion method. The results were as follows: 1. When dye penetration scores were compared, no significant differences were observed at each level (Kruskal-Wallis test, p>0.05). 2. Distribution of F and Sr was detected along the root canal dentin in contact with the S-PRG sealer, although this was not observed for the PulpDent sealer. 3. Both sealers of both fresh and set preparations showed antibacterial activity against P. acnes and A. Israelii, whereas activity against E. faecalis was not detected. It was concluded that the prototype S-PRG sealer has the ability to release F and Sr, and that the coronal sealing ability and anti-bacterial capacity of the S-PRG sealer are comparable to those of zinc oxide-eugenol sealers.

Journal

  • The Japanese Journal of Conservative Dentistry

    The Japanese Journal of Conservative Dentistry 50(6), 713-720, 2007

    The Japanese Society of Conservative Dentistry

References:  29

Cited by:  7

Codes

  • NII Article ID (NAID)
    110007154308
  • NII NACSIS-CAT ID (NCID)
    AN00191201
  • Text Lang
    JPN
  • Article Type
    Journal Article
  • ISSN
    0387-2343
  • Data Source
    CJP  CJPref  NII-ELS  J-STAGE 
Page Top