1544 ホットプレス成形した竹の強度特性(S11-3 バイオマス由来材料の成形加工と特性評価(3)植物系バイオマスの成形性と強度特性,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境) 1544 Mechanical properties of hot-pressed bamboo

この論文にアクセスする

著者

抄録

Raw bamboo was hot-pressed in order to increase its mechanical properties, such as flexural strength, flexural modulus and impact strength. The hot-pressing conditions were varied in the following range: temperature, room temperature to 220℃: pressure, 5 to 100 MPa. The flexural strength, compressive strength and Izod impact strength increased with increasing molding temperature, showing the maximum peak values at 160℃, but thereafter decreased. Densification at both vascular bundles and parenchyma cells region was achieved by hot-pressing, resulting in the improved mechanical properties.