強磁性共鳴法によるNi_<83>Fe_<17>(011)単結晶薄膜のダンピング定数評価 Damping Constants of Ni_<83>Fe_<17>(011) Single Crystal Thin Films investigated by Q-band Ferromagnetic Resonance

この論文をさがす

著者

抄録

Ni-Fe(011)/MgO(011)単結晶薄膜について、Q-Band(35GHz帯)強磁性共鳴(FMR)装置を用いて、結晶構造の点からGilbertのダンピング定数αの印加磁界角度依存性と膜厚依存性を測定した。膜厚t=10nm,20nmの試料ではα=0.008の一定値を示し結晶方向に依存しなかった。膜厚が5nm以下の試料では膜厚の減少とともに、αは0.008から0.040に上昇し、[01-1]_<Ni-Fe>方向で最大値をとるように2回対称の変化を示した。

Angular dependence of Gilbert's damping constant a for Ni-Fe(011) single-crystal thin films prepared on Mg(011) single-crystal substrates were investigated by employing Q-Band ferromagnetic resonance analysis. The α for 10Onm-thick and 20nm-thick specimen had the constant value of 0.008, which did not depend on the crystal direction. With decreasing the film thickness from 20 to 2nm, the α increased suddenly from 0.008 to 0.040. The 2nm-thick and 5nm-thick specimen had the maximum value of α, when the external field were applied parallel to [01-1]_<Ni-Fe> directions.

収録刊行物

  • 電子情報通信学会技術研究報告. MR, 磁気記録

    電子情報通信学会技術研究報告. MR, 磁気記録 112(294), 5-10, 2012-11-09

    一般社団法人電子情報通信学会

参考文献:  10件中 1-10件 を表示

各種コード

  • NII論文ID(NAID)
    110009642007
  • NII書誌ID(NCID)
    AN10013050
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    0913-5685
  • NDL 記事登録ID
    024149387
  • NDL 請求記号
    Z16-940
  • データ提供元
    CJP書誌  NDL  NII-ELS 
ページトップへ