G030141 高弾性率PBO繊維の圧縮強度特性の評価([G03014]材料力学部門一般セッション(14):機械的特性)

• 川野 優希

  富山県立大学大学院工学研究科

• 堀川 教世

  富山県立大学工学部

• 春山 義夫

  富山県立大学工学部

• 境田 彰芳

  明石工業高等専門学校

• 今道 高志

  滋賀県商工観光労働部新産業振興課

書誌事項

タイトル別名

• G030141 Evaluation of Compressive Strength Properties of High-Modulus PBO Fiber

抄録

In this paper, compressive strength properties of PBO fibers were investigated in direct compression test. Two types of PBO fibers were used in the experiment. One is conventional type of fiber. Another is high modulus type of fiber, and its crystal orientation is higher than conventional type of the fiber. Weibull analysis was performed to describe distribution of compressive strength. It was found that the compressive strength of both PBO fibers were well fitted the Weibull distribution function with 2 parameters. Shape and scale parameters of high modulus type PBO fiber were 8.85 and 238 MPa, respectively. Compressive strength of the high modulus type of PBO fiber showed a slight size effects for both length and diameter direction. Compressive strength of the high modulus type of PBO fiber was higher than that of conventional type of PBO fiber.

収録刊行物

• 年次大会

  年次大会 2011 (0), _G030141-1-_G030141-3, 2011

  一般社団法人 日本機械学会

キーワード

• Compressive Strength
• High Modulus Type
• Crystal Orientation
• Weibull Distribution
• Size Effect

詳細情報

• CRID: 1390282680816681216
• NII論文ID: 110009758786
• DOI: 10.1299/jsmemecj.2011._g030141-1
• ISSN: 24242667
• Web Site: https://www.jstage.jst.go.jp/article/jsmemecj/2011/0/2011__G030141-1/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可