- OS1509 EBSD Observation for Grain Substructure of Creep and Creep-fatigue Damage Process of Mod.9Cr steel
抄録
EBSD(Electron BackScatter Diffraction pattern) observations were conducted on damaged Mod.9Cr steel obtained by the creep and the creep-fatigue tests as well as unused material. In order to quantify accumulated strains due to creep and creep-fatigue damage, "EBSD strain parameter M_<εKAM>" was introduced based on KAM(Kernel Average Misonentation) maps obtained by the EBSD observations. Here, M_<εKAM> was defined as the product of area averaged KAM: KAM_<ave> and boundary spacing/pixel size ratio. As a result, M_<εKAM> showed a good linear correlation with creep strain components for creep and creep-fatigue damaged materials under the optimal magnifications and grain boundary identification conditions in the EBSD observations. Therefore, M_<εKAM> was thought as a good parameter corresponding to the creep strain component. M_<εKAM> was also successfully applied to evaluate the creep strain components in the area containing the vicinity of creep voids and creep-fatigue crack tips on the failed materials by creep and creep-fatigue.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2013 (0), _OS1509-1_-_OS1509-3_, 2013
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205873760640
-
- NII論文ID
- 110009936757
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可