- OS1548 Fatigue Fracture Behavior in CFRP Cross-ply Laminate with a Hole
抄録
Fatigue fracture behavior in two types of laminate specimen ([0_4/90_8/0_4] and [90_4/0_8/90_4]) with a hole in the middle was investigated under cyclic tensile loading. Two parameters were examined and evaluated: an equivalent stiffness and a dissipated energy calculated from hysteresis loop area in one cycle loading. Fatigue damages of specimen surface and around a hole were observed using replicated method and a scanning acoustic microscope (SAM) respectively. Four stages of fatigue damage process were recognized; (I) matrix cracks appeared around a hole and propagated in longitudinal and transverse directions, which led to steep reduction of the equivalent stiffness. (II) inter laminar delamination at 0/90 inter-ply occurred at the initiation sites of matrix cracks, and grew to the edge of the specimen. This brought on increasing area of hysteresis loop and reduction of stiffiiess. (III) inter laminar delamination took place fully in the transverse direction followed by further extension in the longitudinal direction. (IV) when the propagation of inter laminar delamination grew to the gage points of the displacement meter, fatigue loading was sustained by 0 degree layer, i.e.,0 degree fiber.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2013 (0), _OS1548-1_-_OS1548-3_, 2013
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680850593408
-
- NII論文ID
- 110009936796
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可