- GS11 The frequency characteristic on the crack growth rate under corrosion fatigue condition for Ti-6Al-4V thin sheet alloy
抄録
Titanium alloys are one of the main metallic materials for biomedical applications. It is important to clarify the crack growth mechanism under corrosion environment, such as bio-environment. Under corrosive condition, hydrogen embrittlement also may be caused due to hydrogen origination by anodic dissolvent reaction. Therefore, the mechanism of fracture under corrosive condition is complicate because anodic dissolvent and hydrogen embrittlement mechanism are competitively involved. However, the load frequency effect on the crack growth under the corrosive environment for a titanium alloy has not yet been clarified. In this study, the corrosion fatigue crack growth tests of Ti-6Al-4V alloy were conducted, and the load frequency effect on corrosion fatigue crack growth rate was investigated.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2012 (0), _GS11-1_-_GS11-3_, 2012
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205872935424
-
- NII論文ID
- 110009937188
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可